3.4应力腐蚀裂纹>30～50±0.3>3～20±10%2力学性能标准牌号抗拉强度（MPa）屈服强度（MPa）伸长率（%）硬度GB308710335～475≥195≥24/20410～550≥245≥20/GB531020G410～550≥245≥24/20MnG≥415≥240≥22/25MnG≥485≥275≥20/15CrMoG440～640≥235≥21/12Cr2MoG450～600≥280≥20/12Cr1MoVG470～640≥255≥21/12Cr2MoWVTiB540～735≥345≥18/10Cr9Mo1VNb≥585≥415≥20/ASMESA210SA210A-1≥415≥255≥30≤143HBSA210C≥485≥275≥30≤179HBASMESA213SA213T11≥415≥205≥30≤163HBSA213T12≥415≥220≥30≤163HBSA213T22≥415≥205≥30≤163HBSA213T23≥510≥400≥20≤220HBSA213T91≥585≥415≥20≤250HBSA213T92≥620≥440≥20≤250HBDIN17175ST45.8/Ⅲ410～530≥255≥21/15Mo3450～600≥270≥22/13CrMo44440～590≥290≥22/10CrMo910480～630≥280≥20/3化学成分标准牌号化学成分（%）CSiMnPSCrMoCuNiVAlWTiNbNGB3087100.07～0.130.17～0.370.38～0.65≤0.030≤0.0300.3～0.65/≤0.25≤0.30//200.17～0.230.17～0.370.38～0.65≤0.030≤0.0300.3～0.65/≤0.25≤0.30//GB531020G0.17～0.240.17～0.370.35～0.65≤0.030≤0.030≤0.25≤0.15≤0.20≤0.25≤0.0820MnG0.17～0.240.17～0.370.70～1.00≤0.030≤0.030≤0.25≤0.15≤0.20≤0.25≤0.0825MnG0.18～0.240.17～0.370.80～1.10≤0.030≤0.030≤0.25≤0.15≤0.20≤0.25≤0.0815CrMo0.12～0.180.17～0.370.40～0.70≤0.030≤0.0300.80～1.100.40～0.55≤0.20≤0.3012Cr2MoG0.08～0.15≤0.500.40～0.70≤0.030≤0.0302.00～2.500.90～1.20≤0.20≤0.3012Cr1MoV0.08～0.150.17～0.370.40～0.70≤0.030≤0.0300.90～1.200.25～0.35≤0.20≤0.300.15～0.3012Cr2MoWVTiB0.08～0.150.45～0.750.45～0.65≤0.030≤0.0301.60～2.100.50～0.65≤0.20≤0.300.28～0.420.30～0.550.08～0.15B0.002～0.00810Cr9Mo1VNb0.08～0.120.20～0.500.30～0.60≤0.020≤0.0108.00～9.500.85～1.05≤0.20≤0.400.18～0.25≤0.0150.06～0.100.03～0.07ASMESA210SA210A-10.13～0.19≥0.10.45～0.65≤0.030≤0.030SA210C0.18～0.24≥0.10.80～1.10≤0.030≤0.030ASMESA213SA213T110.05～0.150.50～1.00.30～0.60≤0.030≤0.0301.00～1.500.50～1.00SA213T120.05～0.15≤0.500.30～0.61≤0.030≤0.0300.80～1.250.44～0.65SA213T220.05～0.15≤0.500.30～0.60≤0.030≤0.0101.90～2.600.87～1.13SA213T230.04～0.10≤0.500.10～0.60≤0.030≤0.0301.90～2.600.05～0.30≤0.0301.45～1.75B0.0005～0.0060.02～0.08≤0.040SA213T910.08～0.120.20～0.500.30～0.60≤0.020≤0.0108.00～9.500.85～1.05≤0.400.18～0.25≤0.0150.06～0.100.03～0.07SA213T920.07～0.13≤0.500.30～0.60≤0.020≤0.0108.50～9.500.30～0.60≤0.400.15～0.25≤0.0151.50～2.00B0.001～0.0060.04～0.090.03～0.07DIN17175ST45.8/Ⅲ≤0.210.10～0.350.40～1.20≤0.040≤0.04015Mo30.12～0.200.10～0.350.40～0.80≤0.035≤0.0350.25～0.3513CrMo440.10～0.180.10～0.350.40～0.70≤0.035≤0.0350.70～1.100.45～0.6510CrMo9100.08～0.15≤0.500.30～0.70≤0.025≤0.0202.00～2.500.90～1.10≤0.30≤0.30≤0.015合金管理论计算：（外径-壁厚）*壁厚*0.02483=每米的重量。黄南 gb5310-95高压锅炉用无缝钢管。化学成分的试验方法应符合gb222-84《钢及合金化学分析方法》和gb223《钢及合金化学分析方法》的有关规定。APISPEC5CT-1999（套管和油管规范），是美国石油学会（AmericanPetreleumInstiute简称"API"）编制并发布的在世界各地通用。其中：套管：由地表面伸进钻井内，专业销售12Cr1MoVG高压锅炉管，15CrMoG高压合金管，P22合金管，P91合金管性能稳定、安全、可靠、可实现免维护，技术水平已达到国内领先水平，达到国际同类产品先进水平.作为井壁衬的管子，其管子之间通过接箍连接。主要材质为J5 N80、P110等钢级，以及抗硫化氢腐蚀的C90、T95等钢级。其低钢级（J5 N80）可为焊接钢管。油管：由地表面插入套管内直至油层的管子，专业销售12Cr1MoVG高压锅炉管，黄南P91合金管，15CrMoG高压合金管，P22合金管P91合金管，销售设备先进，品种资质齐全，欢迎广大客户前来咨询选购.其管子之间通过接箍或整体连接。其作用于是抽油机将油层石油经油管输送到地面。主要材质为J5 N80、P1 以及抗硫化氢腐蚀的C90、T95等钢级。其低钢级（J5 N80）可为焊接钢管。威海>30～50±0.3>3～20±10%2力学性能标准牌号抗拉强度（MPa）屈服强度（MPa）伸长率（%）硬度GB308710335～475≥195≥24/20410～550≥245≥20/GB531020G410～550≥245≥24/20MnG≥415≥240≥22/25MnG≥485≥275≥20/15CrMoG440～640≥235≥21/12Cr2MoG450～600≥280≥20/12Cr1MoVG470～640≥255≥21/12Cr2MoWVTiB540～735≥345≥18/10Cr9Mo1VNb≥585≥415≥20/ASMESA210SA210A-1≥415≥255≥30≤143HBSA210C≥485≥275≥30≤179HBASMESA213SA213T11≥415≥205≥30≤163HBSA213T12≥415≥220≥30≤163HBSA213T22≥415≥205≥30≤163HBSA213T23≥510≥400≥20≤220HBSA213T91≥585≥415≥20≤250HBSA213T92≥620≥440≥20≤250HBDIN17175ST45.8/Ⅲ410～530≥255≥21/15Mo3450～600≥270≥22/13CrMo44440～590≥290≥22/10CrMo910480～630≥280≥20/3化学成分标准牌号化学成分（%）CSiMnPSCrMoCuNiVAlWTiNbNGB3087100.07～0.130.17～0.370.38～0.65≤0.030≤0.0300.3～0.65/≤0.25≤0.30//200.17～0.230.17～0.370.38～0.65≤0.030≤0.0300.3～0.65/≤0.25≤0.30//GB531020G0.17～0.240.17～0.370.35～0.65≤0.030≤0.030≤0.25≤0.15≤0.20≤0.25≤0.0820MnG0.17～0.240.17～0.370.70～1.00≤0.030≤0.030≤0.25≤0.15≤0.20≤0.25≤0.0825MnG0.18～0.240.17～0.370.80～1.10≤0.030≤0.030≤0.25≤0.15≤0.20≤0.25≤0.0815CrMo0.12～0.180.17～0.370.40～0.70≤0.030≤0.0300.80～1.100.40～0.55≤0.20≤0.3012Cr2MoG0.08～0.15≤0.500.40～0.70≤0.030≤0.0302.00～2.500.90～1.20≤0.20≤0.3012Cr1MoV0.08～0.150.17～0.370.40～0.70≤0.030≤0.0300.90～1.200.25～0.35≤0.20≤0.300.15～0.3012Cr2MoWVTiB0.08～0.150.45～0.750.45～0.65≤0.030≤0.0301.60～2.100.50～0.65≤0.20≤0.300.28～0.420.30～0.550.08～0.15B0.002～0.00810Cr9Mo1VNb0.08～0.120.20～0.500.30～0.60≤0.020≤0.0108.00～9.500.85～1.05≤0.20≤0.400.18～0.25≤0.0150.06～0.100.03～0.07ASMESA210SA210A-10.13～0.19≥0.10.45～0.65≤0.030≤0.030SA210C0.18～0.24≥0.10.80～1.10≤0.030≤0.030ASMESA213SA213T110.05～0.150.50～1.00.30～0.60≤0.030≤0.0301.00～1.500.50～1.00SA213T120.05～0.15≤0.500.30～0.61≤0.030≤0.0300.80～1.250.44～0.65SA213T220.05～0.15≤0.500.30～0.60≤0.030≤0.0101.90～2.600.87～1.13SA213T230.04～0.10≤0.500.10～0.60≤0.030≤0.0301.90～2.600.05～0.30≤0.0301.45～1.75B0.0005～0.0060.02～0.08≤0.040SA213T910.08～0.120.20～0.500.30～0.60≤0.020≤0.0108.00～9.500.85～1.05≤0.400.18～0.25≤0.0150.06～0.100.03～0.07SA213T920.07～0.13≤0.500.30～0.60≤0.020≤0.0108.50～9.500.30～0.60≤0.400.15～0.25≤0.0151.50～2.00B0.001～0.0060.04～0.090.03～0.07DIN17175ST45.8/Ⅲ≤0.210.10～0.350.40～1.20≤0.040≤0.04015Mo30.12～0.200.10～0.350.40～0.80≤0.035≤0.0350.25～0.3513CrMo440.10～0.180.10～0.350.40～0.70≤0.035≤0.0350.70～1.100.45～0.6510CrMo9100.08～0.15≤0.500.30～0.70≤0.025≤0.0202.00～2.500.90～1.10≤0.30≤0.30≤0.015合金管理论计算：（外径-壁厚）*壁厚*0.02483=每米的重量。小直径锅炉管是指两端开孔、截面为空心的钢管，其长度大于周围钢材的长度。按 方法可分为无缝钢管和焊接钢管。钢管的规格是用外形尺寸（如外径或边长）和壁厚来表示的，其尺寸范围很广，从小直径的毛细管到几米直径的大直径管道。钢管可用于管道、热力设备、机械工业、石油地质勘探、集装箱、化工及特殊用途。钢管分为无缝钢管和焊接钢管（带缝）。按截面形状可分为圆管和异形管。圆钢管应用广泛，但也有些方形、矩形、半圆、角形、等边角形、角形等异型钢管。对承受流体压力的钢管进行水压试验，检查其耐压性能和质量。在规定压力下无渗漏、湿润、膨胀为合格。部分钢管应按标准或需方要求进行压接试验、胀接试验、压扁试验等。。概述 制造方法：般小直径锅炉管使用温度在350℃以下，国产管主要采用 20号碳钢热轧管或冷拔管。合金管作为钢铁产品的重要组成部分，因其制造工艺及所用管坯形状不同而分为无缝钢管（圆坯）和焊接钢管（板，带坯）两大类。
5354.8120未断高压锅炉管主要用来制造高压和超高压锅炉的过热器管、再热器管、导气管、主蒸汽管等。高压锅炉管行业供求趋势总体平稳，黄南P22合金管，各具体子行业供求状况将进步分化。业内人士指出，奥氏体分稳定，要冷却到较低温度(约400℃)才能变为马氏体。粗大的马氏体组织脆而硬，接头又处在复杂应力状态下。同时，焊缝冷却过程中氢由焊缝向近缝区扩散，氢的存在促使了马氏体脆化，很容易在淬硬区产生冷裂纹。服务为先Q是汉字"屈服"的汉语拼音的个字母，表示屈服强度345就是屈服强度的具体数值:345MPa后面的c是该强度级别的钢的质量等级符号，般分A，B，CD，E等级别(越往后级别越高)注意：A，，B，C，D，E个级别并不是与前面的个钢号对应，而是质量级别，主要区别是冲击功的要求不同：Q345-A：不要求冲击功Q345-B：要求常温冲击功Q345-C：要求0℃的冲击功Q345-D：要求-20℃的冲击功Q345-E：要求-40℃的冲击功可以看出：后面的钢号可以在低温下使用Q345C合金管的具体化学成分为：C≤0.2%，Mn1.0-1.6%Si≤0.55%，S≤0.35%，P≤0.35%，V0.02-0.15%，Nb0.015-0.06%，Ti0.02-0.2%，AL≥0.015%机械性能为：屈服强度：≥345MPa（厚度16mm以下）3.4应力腐蚀裂纹
对应的88年以前的旧牌号有:16Mn、12MnV、14MnNb、16MnRe、18Nb个牌号合并而成)标准要求Ni≤0.40 进口锅炉管道的物理性能检验和指标按合同规定的有关标准执行。电力用锅炉管主要用来制造高压和超高压锅炉的过热器管、再热器管、导气管、主蒸汽管等。黄南钯管纯化氢的原理是在300—500℃下把待纯化的氢通入钯管的侧时氢被吸附在钯管壁上由于钯的4d电子层缺少两个电子它能与氢生成不稳定的化学键(钯与氢的这种反应是可逆的)在钯的作用下4消除氢脆减少T22合金钢管中渗氢的数量，必须尽量减少高强度/高硬度钢制T22合金钢管的酸洗因为酸洗可加剧氢脆。在除锈和氧化皮时，尽量采用喷砂抛丸的方法，专业销售12Cr1MoVG高压锅炉管，15CrMoG高压合金管，P22合金管，P91合金管高价销售，上门服务，现场结算，诚信经营!若洛氏硬度等于或大于HRC32的T22合金钢管进行酸洗时，必须在制定酸洗工艺时确保T22合金钢管在酸中浸泡的时间长不超过10分钟。并应尽量降低酸液的浓度，并保证零件在酸中浸泡的时间不超过10分钟；在除油时，采用清洗剂或溶剂除油等化学除油方式，黄南15CrMoG高压合金管金融贡献的利润，渗氢量较少，若采用电化学除油，先阴极后阳极，高强度T22合金钢管不允许用阴极电解除油；在热处理时严格控制甲醇和丙烷的滴注量；在电镀时，碱性镀液或高电流效率的镀液渗氢量较少。采用低氢扩散性和低氢溶解度的镀涂层般认为，在电镀Cr、Zn、Cd、Ni、Sn、Pb时，渗入钢件的氢容易残留下来，而Cu、Mo、Al、Ag、Au、W等T22合金钢管镀层具有低氢扩散性和低氢溶解度，渗氢较少。在满足产品技术条件要求的情况下，可采用不会造成渗氢的涂层，如机械镀锌或无铬锌铝涂层，不会发生氢脆，附着力好，镀前应进行回火处理，回火消除应力实际上可以减少零件内的陷阱数量，从而减轻发生氢脆的隐患。控制镀层厚度，由于镀层覆盖在紧固件表面，镀层在定程度上会起到氢扩散屏障的作用，黄南15CrMoG高压合金管产品出口实现新突破，这将阻碍氢向紧固件外部的扩散。当镀层厚度超过2.5μm时，氢从紧固件中扩散出去就非常困难了。因此硬度<32HRC的紧固件，镀层厚度可以要求在12μm；硬度≥32HRC的高强度螺栓，镀层厚度应控制在8μmmax。这就要求在产品设计时，必须考虑到高强度螺栓的氢脆风险，合理选择镀层种5除锈：除锈等级，对于合金管常用的环氧类，乙烯类，酚醛类等防腐涂料的施工工艺，般要求的都是将合金管表面达到近白级，通过实践得出的证明是，用这种除锈等级几乎可以除掉所有的氧化皮，专业销售12Cr1MoVG高压锅炉管15CrMoG高压合金管，P22合金管，P91合金管，量大从优，质优价廉.耐火-防水-耐高温，结实耐用，安全可靠.锈还有 的污物充分的满足了防腐层和合金管的附着力要求，而喷射除锈工艺可以用较低的费用就可以稳定可靠的使质量达到近白级的条件。第：想要使除锈效果达到理想的效果，需要根据合金管表面的硬度，原始锈蚀程度，要求的表面粗糙度，涂层类型等来选择磨料，黄南15CrMoG高压合金管，单层环氧，层或者是层聚乙烯涂层，要想达到理想的除锈效果，需要采用钢砂和钢丸的混合磨料。因为钢丸有强化钢表面的作用，钢砂有刻蚀钢表面的作用。第：想要获得较好的均匀清洁度和粗糙度的分布，磨料的粒径和配比的设计是相当重要的，因为粗糙度太大是很容易造成防腐层在锚纹尖峰处变薄的同时会因为锚纹太深，就容易在防腐的过程中形成气泡，严重影响着防腐层的性能。（在实际的操作中，磨料中的钢砂和钢丸的理想比例是很难达到的）第：在喷射处理之前，还可以用加热炉对管体预热至40-60摄氏度，使合金管的表面保持干燥的状态，因为合金管表面是不含油脂等污垢的，这样可以增强除锈的效果，另外，干燥的合金管表面也是有利于钢丸，钢砂和锈和氧化皮的分离的，这样就会使才除锈后的合金管表面更加的洁净。注意：A，BC，D，E个级别并不是与前面的个钢号对应，，而是质量级别，主要区别是冲击功的要求不同：Q345-A：不要求冲击功Q345-B：要求常温冲击功Q345-C：要求0℃的冲击功Q345-D：要求-20℃的冲击功Q345-E：要求-40℃的冲击功可以看出：后面的钢号可以在低温下使用Q345C合金管的具体化学成分为：C≤0.2%Mn1.0-1.6%，Si≤0.55%，吕梁孝义耐磨板锤企业逐渐认可互联网的传播效应，S≤0.35%，P≤0.35%，V0.02-0.15%，Nb0.015-0.06%，AL≥0.015%机械性能为：屈服强度：≥345MPa（厚度16mm以下）插销试验表明，T91钢有较大冷裂倾向，选取预热200～250℃，可有效防止冷裂纹产生。